| Title:Effect of 10% Triphala as final irrigant on pushout bond strength of Bioroot RCS to root canal dentin: An Invitro study |
| Abstract:BACKGROUNDː Irrigants used during chemo-mechanical preparation flush these loose debris out, act as an antimicrobial agent, and dissolve the inorganic & organic component of smear layer leading to improved adaption between sealer to the dentinal walls. The present study evaluated the effect of 10% Triphala as the final irrigant on the Push-out bond strength (POBS) of BioRootTM RCS to Root canal dentin. METHODSː36 single-rooted teeth were decoronated and standardized to length 16± 1. Root canals were prepared till F3 ProTaper Gold using 2.5% Sodium Hypochlorite (NaOCl) as the irrigant. Following the radicular preparation, the roots were allocated into 3 groups (n=12), namely 10% Triphala, 17% EDTA and 0.9% Saline and were used as final test irrigants. The samples were then horizontally sectioned into 2mm slices and one sample from the middle third was taken and was filled with BioRootTM RCS sealer using a hand plugger. After 1 week, the tooth sections were subjected to POBS measurement using Universal Testing Machine (UTM). Results were analysed statistically with the help of one-way ANOVA with post-hoc Tukey Honest Significant Different test. RESULTSː The maximum POBS was observed with 17% EDTA (3.569 MPa), followed by 10% Triphala (3.48 MPa) and the minimum was observed with 0.9% Saline group (2.243 MPa). On intragroup comparison, no significant differences were noted between 10% Triphala and 17% EDTA groups. However, both 10% Triphala and 17 % EDTA showed highly significant differences in comparison to 0.9% Saline. Results of the fractographic analysis revealed that out of a total 36 samples, 22.3% showed adhesive failure, 17.1% showed cohesive failure and 60.6% showed mixed failure. CONCLUSIONː Within the limitations of this study, 10% Triphala is comparable to 17% EDTA as the final irrigant with respect to POBS of BioRootTM RCS to root canal dentin. |
| Keywords:Triphala, Bioceramic sealer, pushout bond strength, 17 % EDTA |
| Authors:Neetha Shenoy, Sandya Kini K*, Anirudh Sarda, Prasad Prabhu |
| Paper PDF Link: View full PDF |